| Customization: | Available |
|---|---|
| Color: | White, Black |
| Maximum Voltage: | 35kv |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
1, Description:
0835 cross-linkable semi-conductive shielding compound is used as strippable insulation shield for cross-linked polyethylene insulation power cable rated voltage up to 35KV. It's suitable for high temperature vulcanization processing method. 0835 provides excellence processability, fine surface smoothness, stable volume resistivity, low pre-cure or scorch characteristic, lower stripping force with anti-tearing property, leaving clean surface for insulation after stripped.3, Technical Parameter
| Property | Test Method | Unit | Value |
| Density at 23°C | ASTM D 1505 | g/ cm3 | ≤ 1.13 |
| Tensile Strength (200 mm/min) Tensile Strength Retention (Heat Aging at 135°C after 168h) |
ASTM D 638 | MPA % |
≥ 13 85 |
| Elongation at Break before ageing Elongation Retention (Heat Aging at 135°C after 168h) |
ASTM D 638 | % % |
280 85 |
| Volume Resistivity at 20°C Volume Resistivity at 90°C |
ASTM-D991 | W.cm W.cm |
60 ≤ 600 |
| Hot Set Test Conditions At 200 ±2 °C x 0.2 MPa for 15 min |
IEC 540-14 | ||
| Elongation after loading Permanent Deformation |
% % |
≤ 60 ≤ 2 |
|
| Moisture Content | KARL FISCHER | ppm | ≤ 500 |
| Brittleness Temperature | ASTM-D746 | -40°C | |
| Stripping Force | Q/TNYM 1-2012 | N/cm | 15 |
| Zone | Zone 1 | Zone 2 | Zone 3 | Zone 4 | Flange | Tube | Screw |
| Temperature Range°C | 80-85 | 90-95 | 100-105 | 105-110 | 105 | 105 | 50-55 |
4,Storage:
Should be stored at room temperatures between 10~30°C. Recommended maximum storage period in dry and clean are is 12 months unopened and in original packaging after the manufacture.