Semi-Conductive Water 0.25 mm Blocking Tape for Electrical Cable and Opgw in China

• Customization: Available
• Color: White
• Material: Yarn
• Thickness: 0.1mm-0.5mm
• Tensile Strength: More Than 18n/Cm
• Elong-Ation: More Than 12%
• Short Term Stability: 230 Celsius Degrees
• Long Term Stability: 90 Celsius Degrees
• Moisture Conten: Less Than 6%
• Type: Insulation Tape
• Chemistry: Waterproof
• Transport Package: Wood Package
• Specification: Customized
• Trademark: Reliable
• Origin: China

Product Description

Product Name:
Water-blocking Tape

 

Product Description

1, Application and Feature: 

It is a combination of tape, yarn, or coating to prevent longitudinal penetration of water into the cable core .The main principle is to use a kind of polymer that can absorb water and quickly form gel to fill the seepage channel through the expansion of hydrogel. It is widely used In optical fiber cable, data cable, telecom cable and control cable.
Proven high performance of swelling and water blocking
Process friendly
REACH and RoHS compliant


2, Section Diagram:

   Single Sizes


   Double sizes



3,Package
In Roll  ID 76mm-105mm

Product Parameters

4,Technical Parameter:   

Single Side Non-conductivity

Thickness	Mass Per Area	Tensile Strength	Elong- Ation	Swelling Speed	Swelling Height	Short Term Stability	Long Term Stability	Moisture Content
mm	g/m2	N/cm	%	mm/1,0	mm/3,0	ºC	ºC	%
0.1±0.01	40±5	≥18	≥12	≥3	≥4	230	90	≤6
0.15±0.03	60±5	≥20	≥12	≥5	≥8	230	90	≤6
0.18±0.03	65±5	≥25	≥12	≥6	≥9	230	90	≤6
0.20±0.03	70±10	≥30	≥12	≥12	≥12	230	90	≤6
0.25±0.03	80±10	≥30	≥12	≥12	≥12	230	90	≤6
0.30±0.03	90±10	≥35	≥12	≥12	≥12	230	90	≤6

Double Side Non-conductivity

Thickness	Mass Per Area	Tensile Strength	Elong- Ation	Swelling Speed	Swelling Height	Short Term Stability	Long Term Stability	Moisture Content
mm	g/m2	N/cm	%	mm/1,0	mm/3,0	ºC	ºC	%
0.18±0.01	65±10	≥25	≥12	≥4	≥6	230	90	≤6
0.20±0.03	70±10	≥28	≥12	≥6	≥9	230	90	≤6
0.25±0.03	80±10	≥35	≥12	≥8	≥12	230	90	≤6
0.30±0.03	90±10	≥40	≥12	≥10	≥14	230	90	≤6
0.35±0.03	100±10	≥40	≥12	≥10	≥14	230	90	≤6
0.20±0.03	75±10	≥35	≥12	≥10	≥12	230	90	≤6
0.25±0.03	85±10	≥35	≥12	≥12	≥15	230	90	≤6
0.50±0.03	130±10	≥45	≥12	≥12	≥16	230	90	≤6

Single Side Semi-conductivity

Thickness	Mass Per Area	Tensile Strength	Elong- Ation	Swelling Speed	Swelling Height	Surface Resistance	Volume Resistance	Moisture Content
mm	g/m2	N/cm	%	mm/1,0	mm/3,0	Ω	Ω.cm	%
0.25±0.03	90±5	≥25	≥12	≥6	≥8	≤1500	<1x10(6)	≤9
0.30±0.03	100±5	≥30	≥12	≥8	≥12	≤1500	<1x10(6)	≤9
0.35±0.03	110±5	≥35	≥12	≥10	≥14	≤1500	<1x10(6)	≤9
0.40±0.03	130±10	≥40	≥12	≥11	≥15	≤1500	<1x10(6)	≤9
0.45±0.03	140±10	≥45	≥12	≥12	≥16	≤1500	<1x10(6)	≤9
0.50±0.03	160±10	≥50	≥12	≥12	≥18	≤1500	<1x10(6)	≤9
Short Term Stability:230 ºC                                              Long Term Stability: 90C,

Double Side Semi-conductivity

Thickness	Mass Per Area	Tensile Strength	Elong- Ation	Swelling Speed	Swelling Height	Surface Resistance	Volume Resistance	Moisture Content
mm	g/m2	N/cm	%	mm/1,0	mm/3,0	Ω	Ω.cm	%
0.25±0.03	100±5	≥30	≥12	≥7	≥10	≤1500	<1x10(6)	≤9
0.30±0.03	110±5	≥30	≥12	≥8	≥12	≤1500	<1x10(6)	≤9
0.35±0.03	120±5	≥35	≥12	≥9	≥13	≤1500	<1x10(6)	≤9
0.40±0.03	130±10	≥40	≥12	≥10	≥14	≤1500	<1x10(6)	≤9
0.50±0.03	130±10	≥50	≥12	≥12	≥16	≤1500	<1x10(6)	≤9
0.50±0.03	160±10	≥50	≥12	≥13	≥18	≤1500	<1x10(6)	≤9
Short Term Stability(C):230                                              Long Term Stability: 90C,