Easy Operation Nylon Resin Blend Cable Manufacturing Inner Shielding Compound Material

Product Description

Product Description

0535 Cross-linkable Semi-conductive Inner Shielding Compound

1,0535 cross-linkable semi-conductive shielding compound is used as conductor shield and bonded insulation shield forcross-linked polyethylene insulation power cable rated voltage up to 35KV. It's suitable for high temperature vulcanizationprocessing method. 0535 provides fine surface smoothness, good extruding fluidity, low pre-cure or scorch characteristic,stable volume resistivity and compatibility with both copper and aluminum conductors, strong bonding with insulation layer.As 0535 bonded type was added in with special additive, it has excellence compatibility with copper conductor without

formation of copper-oxidation.

Specification

Property	Test Method	Unit	Value
Density at 23°C	ASTM D 1505	g/cm³	≤ 1.10
Tensile Strength (200 mm/min)	ASTM D 638	MPA	≥ 17
Tensile Strength Retention (Heat Aging at 135°C after 168h)	ASTM D 638	%	85
Elongation at Break before ageing	ASTM D 638	%	290
Elongation Retention (Heat Aging at 135°C after 168h)	ASTM D 638	%	85
Volume Resistivity at 20°C	ASTM-D991	W·cm	20
Volume Resistivity at 90°C	ASTM-D991	W·cm	≤ 200
Hot Set Test Conditions At 200 ±2 °C × 0.2 MPA for 15 min	IEC 540-14	—	—
Elongation after loading	IEC 540-14	%	≤ 60
Permanent Deformation	IEC 540-14	%	≤ 2
Moisture Content	KARL FISCHER	ppm	≤ 500
Brittleness Temperature	ASTM-D746	—	-40°C

Processing Conditions

The recommended standard extrusion temperature profiles are as followings--------------------------------Unit: °C

Zone	Zone 1	Zone 2	Zone 3	Zone 4	Flange	Tube	Screw
Temperature Range(°C)	85-90	95-100	105-110	110-115	110-112	110-115	65-70

We suggest using double layer filter mesh with size 40 mesh (350μm).

We recommend hopper drying at 40~60'C for 4 hours to remove moisture before extrusion.

5. Storage

Should be stored at room temperatures between 10~30°C. Recommended maximum storage period in dry and clean areis 12 months unopened and in original packaging after the manufacture.

Other Products

0535 cross-linkable semi-conductive shielding compound is used as conductor shield and bonded insulation shield for 

cross-linked polyethylene insulation power cable rated voltage up to 35KV. It's suitable for high temperature vulcanization 

processing method. 0535 provides fine surface smoothness, good extruding fluidity, low pre-cure or scorch characteristic, 

stable volume resistivity and compatibility with both copper and aluminum conductors, strong bonding with insulation layer.

As 0535 bonded type was added in with special additive, it has excellence compatibility with copper conductor without 

formation of copper-oxidation.

0835 cross-linkable semi-conductive shielding compound is used as strippable insulation shield for cross-linked polyethylene 

insulation power cable rated voltage up to 35KV. It's suitable for high temperature vulcanization processing method. 0835 provides excellence processability, fine surface smoothness, stable volume resistivity, low pre-cure or scorch characteristic, lower stripping force with anti-tearing property, leaving clean surface for insulation after stripped. 

This material is a kind of crosslinkable polyethylene insulation compound. It is made of high quality PE resin, dicumyl

peroxide agent and antioxidant agent by plasticizing granulation. Production process uses the closed system; Loss-in-

weight Feeder which guarantees stable precision of components. It has stable physical and chemical index and good

processing property.

Application: 35kV crosslinkable cable insulation; Maximum working temperature is 90℃.

Grafted elastomer resin is prepared by reactive extrusion method using elastomer resin (PO elastomer, Styrene-olefin elastomer, etc.) as the substrate and maleic anhydride or glycidyl methacrylate as the monomer. Theproduct has the characteristics of good reactivity and good processability, and is applied to modified engineeringplastic(PA, PC, PBT, etc.). As a compatibilizer, it endows materials with excellent compatibility and improves thecomprehensive performance of composite materials. As a toughening agent, it can greatly enhance the toughnessof the material.

Company Profile

JIANGSU RELIABLE INDUSTRY CO., LTD.

JIANGSU RELIABLE INDUSTRY CO. LTD (RLB) was established in the year 2001 in the fast developing city of Changzhou, in Jiangsu the Easter-Central province of China. Since then, RLB has been working dynamically to become a preferred supplier of Wire & Cable materials and a reliable provider of equipment, systems and solutions. RLB leveraged from utilizing technology with its strong experience and knowledge in the industry Standards, to guarantee to offer price-competitive yet premium products directly from its own manufacturing facilities or through the strong  connections and solid joint ventures with other prominent source suppliers located in China.

More Product Recommendations

Today, RLB is highly grateful to its client spread for trusting its extended pool of offered products, ranging from metals (copper, aluminum, and steel), plastics, chemicals, and tapes, as well as heavy machinery, intermediate machinery,auxiliary equipment and spare-parts & tools.

Packaging & Shipping

FAQ

1. Are you a manufacturer or trading company?
We are a professional manufacturer. We can control your order from the first begining to the last. 

2. How can I get a sample to test your quality?
The samples are free for you. New clients are expected to pay for the courier cost.
 
3. What's your Minimum Order Quantity?
Normally 500KGS . You'd better order a suitable quantity to avoid the high freight.
Sea transportation is the best option.
 
4. Can I get a discount?
It depends on your quantity, We can make a discount and afford the freight. Pls kindly contact us.